Product Name: Hastelloy/C-276/UNS N10276
International name: Hastelloy, C-276, INCONEL Alloy C-276, HC-276, Hastelloy C-276, UNS N10276, W.-Nr. 2.4819, ATI C-276, Nicrofer 5716 hMoW-Alloy C-276, NAS NW276
Executive standards: ASTM B575/ASME SB-575, ASTM B574/ASME SB-574, ASTM B622/ASME SB-622, ASTM B619/ASME SB-619, ASTM B366/ASME SB-366, ASTM B564/ASME SB-564
Main components: carbon (C) ≤ 0.01, manganese (Mn) ≤ 1.00, nickel (Ni) ≥ 57, silicon (Si) ≤ 0.08 phosphorus (P) ≤ 0.04, sulfur (S) ≤ 0.03, chromium (Cr) 14.5～ 16.5, iron (Fe) 4.0～7.0, molybdenum (Mo) 15.0～17.0, tungsten (W) 3.0～4.5, cobalt (Co) ≤2.5
Physical Properties: C-276 Density: 8.9g/cm3, Melting Point: 1325-1370 ℃, Magnetic: No
Heat treatment: heat preservation between 1150-1175℃ for 1-2 hours, rapid air cooling or water cooling.
Mechanical properties: Tensile strength: σb≥690Mpa, yield strength σb≥275Mpa: Elongation: δ≥40%, hardness≤100 (HRB)
Corrosion resistance and main use environment:
Hastelloy C-276 is a nickel-chromium-molybdenum alloy containing tungsten, an extremely low silicon carbon content, and is considered a universal corrosion resistant alloy. The alloy has the following characteristics: ①In the state of oxidation and reduction, it has excellent corrosion resistance to most corrosive media. ②It has excellent resistance to pitting corrosion, crevice corrosion and stress corrosion. The higher content of molybdenum and chromium makes the alloy resistant to chloride ion corrosion, and the tungsten element further improves the corrosion resistance. At the same time, C-276 alloy is one of the only materials resistant to the corrosion of wet chlorine gas, hypochlorite and chlorine dioxide solutions, and has a significant effect on high-concentration chloride salt solutions such as ferric chloride and cupric chloride. Corrosion resistance. It is suitable for sulfuric acid solutions of various concentrations and is one of the few materials that can be used in hot concentrated sulfuric acid solutions.
Supporting welding materials and welding process: Hastelloy C-276 welding materials use ERNiCrMo-4 welding wire and ENiCrMo-4 welding rod, the welding material size is Φ1.0, 1.2, 2.4, 3.2, 4.0, the origin is: Hastelloy, the United States SMC and Deutsche Nickel, welding procedures and instructions are welcome to call.
Inventory: C-276 alloy plate stock size is 0.38mm-45mm, bar stock stock size is Φ12mm-Φ320mm, pipe fittings and others can be customized according to customer requirements. The material origins mainly include Haynes in the United States, SMC in the United States, ATI in the United States, and Thyssenkrupp VDM in Germany. Provide original material certificate, customs declaration and certificate of origin.
Application fields: power plant desulfurization and denitration environmental protection, petrochemical equipment, coal chemical industry, fluorine chemical industry, fine chemical industry, PTA, aviation manufacturing, offshore platform, seawater desalination, papermaking machinery, pharmaceutical equipment, heat exchange equipment, electrochemistry, metallurgy, nuclear energy, Chlor-alkali, shipbuilding, cement manufacturing, composite panels, acetic anhydride, salt production, plate heat exchangers, bellows expansion joints and other industries and products.