Ti‐15V‐3Cr‐3Sn‐3Al Titanium Plate
1.Ti‐15V‐3Cr‐3Sn‐3Al titanium plate is a metastable beta titanium alloy that offers substantial weight reductions over other engineering materials. If used in the solution treated condition the alloyhas excellent cold formability. In the aged condition, the alloy has high strength. The alloy is acceptable for use up to 550°F (228°C).
2.Standard：AMS4914.
3.Production period :7-30 days.
4.Payment terms :T/T,L/C.
Description
Ti‐15V‐3Cr‐3Sn‐3Al titanium plate Description
Ti‐15V‐3Cr‐3Sn‐3Al titanium plate also calls titanium 15-3-3-3 plate is a metastable beta titanium alloy that offers substantial weight reductions over other engineering materials. If used in the solution treated condition the alloyhas excellent cold formability. In the aged condition, the alloy has high strength. The alloy is acceptable for use up to 550°F (228°C).
Applications
Springs
Fasteners
Aerospace applications
Chemcial component
Typical Vanadium: 14.0-16.0
Chromium: 2.5-3.5
Tin: 2.5-3.5
Aluminum: 2.5-3.5
Oxygen: 0.13max
Carbon: 0.05max
Nitrogen: 0.05max
Hydrogen: 0.015max
Iron: 0.25max
Residuals each 0.10 max, total 0.40 max
Physical Properties
Density, 0.172 lbs/in³, 4.76 g/cm³
Modulus of Elasticity, ksi (MPa) 11.9 x 10³ (82 x 10³)in tension
Melting Point: 3034°F (1668°C)
Mechanical Properties at Room Temperature
Properties: Annealed (1450°F – A.Q.)
Ultimate Tensile Strength: 102 KSI min (703 MPa min)
Yield Strength (0.2% offset): 100 KSI min (690 MPa min)
Elongation: 12%min
Tempered:
Ti‐15V‐3Cr‐3Sn‐3Al titanium plate Can Be age hardened at 900-1000°F, aging time varies from 2-3 Hours.
Aged Properties:Typical
Aging Temp/Time: 1000°F /8 Hours
Ultimate Tensile Strength: 145 KSI min (1000 MPa min)
Yield Strength (0.2% offset): 170 KSI min (1172 MPa)
Elongation: 7%min Aging Temp/Time: 1100°F /8 Hours
Ultimate Tensile Strength: 170 KSI min (1172 MPa min)
Yield Strength (0.2% offset): 160 KSI min (1103 MPa min)
Elongation: 5%min
Aging Temp/Time: 1275°F /8 Hours
Ultimate Tensile Strength: 180 KSI min (1241 MPa min)
Yield Strength (0.2% offset): 170 KSI min (1172 MPa min)
Elongation: 5%min
Additional Properties
Corrosion Resistance Refer to NACE (National Association of Corrosion Engineers) for recommendations.
Finishes
Inquire with Ulbrich Wire
Forms
Continuous Coils
Cut to lengths
Precision cutting
Heat Treatment
Ti‐15V‐3Cr‐3Sn‐3Al titanium plate can be hardened by aging
About Us
Baoji Jufuti Non-ferrous Metals Co,Ltd. for short ( JFTI Titanium Industry ) is an integrated high-tech enterprise and worldwide supplier specialized engaged in research,production and development of titanium,nickel ,zirconium and other Non-ferrous metal alloys in baoji city which knows as "the titanium valley" in China.
Our main products are various specifications of titanium and titanium alloy meets international and American Standard ASTM,ASME,AMS, products are including titanium plate, tube,bar, wire ,forgings and titanium Sintered filter rod, titanium aerator, titanium filter plate，titanium pipe fittings ,titanium fasteners ,titanium CNC processing parts and nickel & zirconium tube ,plate ,bar & other non-ferrous metals etc.
We have factory with area more than 6000 square meters,equipped with advanced large-scale facilities such as VAR Furnace,hydraulic press,forging press,CNC machines and plasma Arc welder.our products are widely used in industry such as aerospace,medical,chemistry,automobile,ship-Building and other fields,our clients are covered all over the world such as USA ,Canada ,UK, Germany, France, Spain ,Turkey, Saudi Arabic,Brazil,Korea,India,Russia,Netherlands,Czech republic ,Indonesia ,Vietnam etc.
JFTI has achieved international quality and management standards ISO9001:2015,AS9100D,GJB9001C:2007 certifications.
Hot Tags: ti‐15v‐3cr‐3sn‐3al titanium plate, China, suppliers, manufacturers, factory, customized, wholesale, low price, for sale, in stock, hot sale, made in China